電工鋼硅鋼片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Since it is a functional material, its performance testing also revolves around "function". These indicators are often mentioned in trade and processing processes, and a brief understanding can help everyone better carry out their work. The performance testing of electrical steel mainly includes the following aspects: magnetic inspection, stacking coefficient inspection, coating adhesion inspection, repeated bending inspection, size and shape surface inspection, and conventional mechanical property inspection. In addition to the types of products listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, which are used as intermediate and intermediate grade High frequency motors and transformers, as well as pulse transformers, etc； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding. Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength. Magnetic induction strength is the number of magnetic lines passing through a unit cross-sectional area of the iron core, also known as magnetic flux density. It represents the material‘s magnetization ability, measured in T. The magnetic induction strength of electrical steel plates is high, and the excitation current (also known as no-load current) of the iron core is reduced. Copper and iron losses are also reduced, which can save electrical energy. When the power of the motor and transformer remains constant, the magnetic induction intensity is high, and the design Bm can be increased. The cross-sectional area of the iron core can be reduced, which reduces the volume and weight of the iron core, and saves the amount of electrical steel plates, wires, insulation materials, and structural materials used. This can reduce the total loss and manufacturing cost of the motor and transformer, and is beneficial for the manufacturing, installation, and transportation of large transformers and motors. The main requirements for the performance of silicon steel are: 1. Low iron loss is the most important indicator of the quality of silicon steel sheets. Various countries classify grades based on iron loss values, with the lower the iron loss, the higher the grade. 2. Under strong magnetic fields, the magnetic induction intensity (magnetic induction) is high, which reduces the volume and weight of the iron core of the motor and transformer, saving silicon steel sheets, copper wires, and insulation materials. 3. The surface is smooth, flat, and the thickness is uniform, which can improve the filling coefficient of the iron core. 4. Good lamination performance is more important for manufacturing micro and small electric motors. 5. The adhesion and weldability of the surface insulation film are good, which can prevent corrosion and improve the punching performan

電工鋼硅鋼片寶鋼可以為客戶(hù)提供性能數(shù)據(jù)原始曲線(xiàn)和其他形式的數(shù)據(jù)。GB20052-2020新能源效率一級(jí)產(chǎn)品S15-M-200/10、河南南陽(yáng)附近S15-M-400/10變壓器成功投產(chǎn)用高等級(jí)GO電工鋼B18R055制造，B20R060，其空載損耗和負(fù)載損耗均滿(mǎn)足新的1級(jí)變壓器的要求。寶鋼高級(jí)晶粒取向電工鋼B27R090成功應(yīng)用于雙百萬(wàn)變壓器的制造ODFPS-1000000/1000用于超高壓交流輸電項(xiàng)目包括空載損耗在內(nèi)的所有變壓器特性，空載電流和噪聲符合設(shè)計(jì)要求。寶鋼優(yōu)質(zhì)晶粒取向硅鋼B23R075已成功應(yīng)用于轉(zhuǎn)爐生產(chǎn)昌吉-古泉±1100kV特高壓直流輸電變壓器 電網(wǎng)項(xiàng)目?？蛰d損耗、河南南陽(yáng)附近空載電流和噪音變壓器的各項(xiàng)性能完全符合技術(shù)要求。 無(wú)機(jī)涂層，S/T2 涂層為磷酸鹽和二氧化硅為主的無(wú)機(jī)成分混合物。該涂層具有較高的耐熱性，在干的氮?dú)饣蛘吒傻牡獨(dú)浠旌媳Ｗo(hù)氣氛中可以承受 850℃應(yīng)力退火。對(duì)絕緣油、河南南陽(yáng)附近清漆、河南南陽(yáng)附近機(jī)械油、河南南陽(yáng)附近制冷氣體等有高耐腐性。 無(wú) Cr 環(huán)保涂層,H,涂層成分中不含 Cr 元素