電工鋼硅鋼片In addition to the types listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, used for medium and high-frequency motors, transformers, and pulse transformers； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding.Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength [1] [2]. The requirements for the performance of electrical steel plates are as follows:Low core loss (PT)Iron core loss refers to the ineffective electrical energy consumed by an iron core when magnetized in an alternating magnetic field of ≥ 50Hz, abbreviated as iron loss, also known as alternating loss, and its unit is W/kg. The ineffective electrical energy consumed due to various obstacles caused by magnetic flux changes not only loses electrical energy through the heating of the iron core, but also causes temperature rise of the motor and transformer. The iron loss (PT) of electrical steel includes three parts: hysteresis loss, eddy current loss (Pe), and anomalous loss (Pa). Electrical steel plates have low iron loss, which can save a lot of electricity, prolong the operating time of motors and transformers, and simplify cooling devices. Due to the iron loss of electrical steel plates, which accounts for 2.5％ to 4.5％ of the annual electricity generation in various countries, countries always try their best to reduce iron loss in the production of electrical steel plates, and use iron loss as the most important indicator to assess the magnetic properties of products. The iron loss value of products is used as the basis for classifying product grades. Cold rolled oriented electrical steel: Cold rolled oriented electrical steel is a high-end product in the field of electrical steel. Compared with cold rolled non oriented electrical steel, its magnetism has strong directionality； It has superior high magnetic permeability and low loss characteristics in the direction of easy magnetization rolling. The iron loss of oriented steel strip in the rolling direction is only 1/3 of that in the transverse direction, and the ratio of magnetic permeability is 6:1. Application: The main purpose of cold-rolled oriented silicon steel strip is for transformer manufacturing.Full process cold rolled non oriented silicon steel coating: The surface of the full process cold rolled silicon steel is coated with a semi transparent insulation coating, which has different codes in different standards. Taking Baosteel‘s Q/BQB 480 2014 as an example:

電工鋼硅鋼片：密度用于計算磁性能和疊裝系數的約定密度為 7.65×103 kg/m3。7.4.2 疊裝系數產品的小疊裝系數應符合表 3、泰州靖江同城表 4、泰州靖江同城表 5、泰州靖江同城表 6、泰州靖江同城表 7、泰州靖江同城表 8 和表 9 的規(guī)定。7.4.3 彎曲次數產品平行于軋制方向的小彎曲次數應不小于 1 次。供方如能保證，可不進行該試驗。7.4.4 由內應力引起的剪切邊的偏差產品應盡可能量避免出現內應力。根據需方要求，并在合同中注明，可對寬度不小于 500mm 的材料（縱切分條后的材料）檢測由內應力引起的剪切邊偏差，其縫隙測量值應不超過 1mm。供方如能保證，可不進行該試驗。8 檢驗和試驗8.1 一般要求8.1.1 按本文件簽訂訂貨協(xié)議時，用戶可按GB/T 17505規(guī)定進行規(guī)定檢驗和試驗或非規(guī)定檢驗和試驗。然而，對于非規(guī)定檢驗和試驗，制造方應提供所需產品的比總損耗值和磁極化強度值。8.1.2 當按規(guī)定檢驗和試驗訂貨時，用戶應明確 GB/T 18253 中的檢驗文件的類型。

電工鋼硅鋼片硅鋼是一種硅鐵合金。用硅鋼軋制的片材是電工領域中應用廣的軟磁材料，因而硅鋼片又稱電工鋼片。硅鋼片廣泛用于電動機、發(fā)電機、變壓器、扼流圈、電磁機構、繼電器及測量儀表中電機工業(yè)大量使用厚度為0.35～0.50mm的硅鋼片,用于：中型旋轉機，壓縮電機，通用馬達，小型精密電機，電動汽車，壓縮機，通用電機，電源變壓器，精密變壓器，節(jié)能電機，焊機變壓器，穩(wěn)壓器，磁性密封器，加速器用電磁鐵，汽車電機等；在電信高頻技術中常用0.05~0.20mm的薄帶鋼片,以便更有效地降低渦流損耗。熱軋硅鋼片厚度為0.35～0.50mm，密度為7.55～7.70g/cm3,多用于大、中、小型交、直流電動機；冷軋無取向硅鋼片厚度為0.35～0.50mm，密度為7.65～7.75g/cm3，多用于大型交流發(fā)電機、電動機，大、中、小型交、直流電動機；冷軋取向硅鋼片厚度為0.23mm 0.27mm 0.3mm 0.35mm，密度為7.65g/cm3,多用于電力變壓器、油浸式變壓器，干式變壓器，電抗器、磁放大器等；冷軋取向薄帶厚度為0.05～0.20mm，多用于無線電高頻變壓器。