低溫壓力容器用鋼板及超低溫鋼SA203E規(guī)格8-100mm，09MnNiDR 規(guī)格8-120mm,15MnNiDR規(guī)格8-120mm,16MnDR規(guī)格8-120mm。 壓力容器用鋼板16MnR、20R、15CrMoR、15MnVR、SA516Gr60、SA516Gr70、20g、SA285GrC、16Mng、410B、07MnNiMoVDR、SA387Gr22CL2、SA387Gr22CL2、SA387Gr11CL2；AISI4140,SA285GrCM,SB410,KP42,Q245R,Q345R,SPV355,Q370R,A515Gr70，A516Gr60，A516Gr70，P235GH，P295GH,P355GH,19Mn6,15Mo3,16Mo3,A537CL1,sa622GrC,18MnMoNR,A48CPR,A515Gr65,A516Gr65,SA612M, A537CL2,SB450 壓力容器用鋼板和鍋爐汽包板 20g,16Mng,15CrMog,12Cr1MoVg,19Mng,22Mng,13MnNiCrMoNbg,20R.16MnR,15MnVR,15CrMoR,13MnNiMoNbR, 15MnNbR,15MnVNR,16MnDR,09MnNiDR,15MnNiDR,12Cr2Mo1R,14Cr1MoR,07MnCrMoVR,07MnNiCrMoVDR, 15MnNiDR,SB410,SB450,SGV480,SBV1A,SBV1B,SBV2,SBV3,SEV245,SEV295,SEV345,10CrMo910,15Mo3, 13CrMo44,19Mn6,BHW35,13MnNiMo54,1Cr05Mo,2.25Cr1Mo,1.25Cr0.5Mo,(S)A299M,(S)A515M(Gr.60,65,70), (S)A204M(Gr,A,B,C),(S)A387M(Gr11,12,22),(S)A537M(GL.1,GL.2),(S)A622M(Gr.A,B,C),(S)A302M(Gr.A,B,C), (S)A737M(Gr.B,C),(S)A738M(Gr.A,B,C),(S)A533M(I,II),P235GH,P265GH,P295GH,P355GH,16Mo3,13CrMo4-5,10CrMo9-10,11CrMo9-10,A42,A52,20MnHR,20HR,16MnHR,161G430,WDB620 鍋爐容器鋼板Q245R-20G-Q345R現(xiàn)貨厚度齊全

冶煉方法 提高鋼水純凈度 在現(xiàn)有條件下，提高鋼水純凈度，有兩個關(guān)鍵的地方，首先是爐前冶煉操作的強化控制，即采用優(yōu)化設(shè)計的氧槍噴頭及音頻控制造渣技術(shù)，加上煉鋼工的經(jīng)驗輔助，在確保脫S、P的前提下，盡可能減少鋼中含氧量；出鋼過程采用擋渣球+擋渣帽雙擋渣工藝，減少轉(zhuǎn)爐渣進入鋼包，同時加入具有脫S作用的鋼包覆蓋劑和鋼水凈化劑。另外，在爐后精煉工序采用底吹氬強制攪拌措施與喂線工藝結(jié)合確保鋼水中的夾雜物上浮，加強鋼包中渣鋼界面的反應(yīng)，進一步脫除S、P，降低鋼中氧含量并改善夾雜物的形態(tài)，提高鋼水純凈度。 冶煉及精煉工藝 濟南鋼鐵集團總公司（簡稱濟鋼）20g的開發(fā)十幾年前就進行過，但限于當(dāng)時的工藝設(shè)備裝備水平，鋼板性能不穩(wěn)定，常有冷彎及時效性能不合的問題出現(xiàn)。著重針對冷彎及時效性能改善、低溫沖擊韌性保證方面采取以下措施： (1)調(diào)整內(nèi)控成分，提高錳含量下限到0.65%。 (2)采用喂線、調(diào)溫、吹氬“三位一體”的精煉操作。 (3)嚴(yán)格控制澆注溫度。 (4)微合金化元素Ti的含量由0.003%提高到0.008%以上。(5)采用全程保護澆注工藝，減少N的吸收。 調(diào)整鋼的內(nèi)控成分 根據(jù) 標(biāo)準(zhǔn)規(guī)定，在冶煉20g(Ti)鋼時，制定了內(nèi)控成分，首先碳在不變（0.12%～0.20%）的情況下，提高了錳的下限成分，由此使鋼的強度等性能指標(biāo)在充分保證的前提下，韌性有所提高，同時由于純凈度提高，使冷彎性能大大改善，也使鋼板的焊接性能得到保證。通過增加Ti含量，改變了N在鋼中的形態(tài)，形成了TiN化合物，提高了鋼的時效性。20g(Ti)鋼的冶煉內(nèi)控成分見表 鍋爐容器鋼板Q245R-20G-Q345R現(xiàn)貨厚度齊全