電工鋼硅鋼片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating

電工鋼硅鋼片：供貨形式產(chǎn)品以卷供貨，簡稱鋼卷。當(dāng)訂貨合同中未注明邊緣狀態(tài)時(shí)，產(chǎn)品按切邊狀態(tài)供貨。6.2.1 鋼卷的重量應(yīng)符合訂貨要求，卷重一般為 2.00～6.00 噸。6.2.2 鋼卷通常以切邊狀態(tài)交貨。用戶有特殊要求時(shí)，通過協(xié)議可以以不切邊狀態(tài)交貨。6.2.3 鋼卷內(nèi)徑應(yīng)在 500mm～520mm 范圍內(nèi)，內(nèi)徑值為 508±5mm。6.2.4 鋼卷應(yīng)由同一寬度的鋼帶連續(xù)、浙江湖州本地緊密卷繞，卷的側(cè)面應(yīng)盡量平直，自重下不塌卷。Q/BQB 485－202156.2.5 產(chǎn)品可能由于去除缺陷而產(chǎn)生接帶或焊縫，接帶或焊縫處應(yīng)作標(biāo)記，接帶或焊縫前后部分應(yīng)為同一牌號，且不超過 2 處，焊縫間鋼帶長度應(yīng)不小于 200 米。6.2.6 除無涂層系列產(chǎn)品之外，產(chǎn)品兩面涂有絕緣涂層。6.2.7 用戶有特殊要求時(shí)，應(yīng)符合訂貨協(xié)議。

電工鋼硅鋼片硅鋼是一種硅鐵合金。用硅鋼軋制的片材是電工領(lǐng)域中應(yīng)用廣的軟磁材料，因而硅鋼片又稱電工鋼片。硅鋼片廣泛用于電動(dòng)機(jī)、發(fā)電機(jī)、變壓器、扼流圈、電磁機(jī)構(gòu)、繼電器及測量儀表中電機(jī)工業(yè)大量使用厚度為0.35～0.50mm的硅鋼片,用于：中型旋轉(zhuǎn)機(jī)，壓縮電機(jī)，通用馬達(dá)，小型精密電機(jī)，電動(dòng)汽車，壓縮機(jī)，通用電機(jī)，電源變壓器，精密變壓器，節(jié)能電機(jī)，焊機(jī)變壓器，穩(wěn)壓器，磁性密封器，加速器用電磁鐵，汽車電機(jī)等；在電信高頻技術(shù)中常用0.05~0.20mm的薄帶鋼片,以便更有效地降低渦流損耗。熱軋硅鋼片厚度為0.35～0.50mm，密度為7.55～7.70g/cm3,多用于大、中、小型交、直流電動(dòng)機(jī)；冷軋無取向硅鋼片厚度為0.35～0.50mm，密度為7.65～7.75g/cm3，多用于大型交流發(fā)電機(jī)、電動(dòng)機(jī)，大、中、小型交、直流電動(dòng)機(jī)；冷軋取向硅鋼片厚度為0.23mm 0.27mm 0.3mm 0.35mm，密度為7.65g/cm3,多用于電力變壓器、油浸式變壓器，干式變壓器，電抗器、磁放大器等；冷軋取向薄帶厚度為0.05～0.20mm，多用于無線電高頻變壓器。